90 membrane in brake system
Description
Diaphragms are flexible barriers that are commonly used to provide a seal and to isolate an enclose between a moving and stationary part. One example of an application where a diaphragm is used is with a piston working within a cylinder.
The product involves a reprocessing of finished products and manufacturing methods to keep the performance (breaking strength, elongation at break, heat shrinkage rate) same in both warp and weft, to ensure excellent properties of the automobile brake air chamber and other rubber products.
Feature
Same structure in both warp & weft
Same physical properties in both warp & weft
Same adhesion level in both warp & weft
Application
The fabrics are widely used as the reinforced materials in the automobile brake system and other rubber moulds with high stability.
Our advantage
We are the biggest manufacturer in China who produces the rubber diaphragm fabrics.
What makes us different is that we have Laser cutting machines and can supply the round pieces directly.It can largely reduce the production cost and enhance the productivity of the customers'.
Specification
EPM60
| ITEM | Standard |
| Warp | Weft |
| Material | Nylon6 | Nylon6 |
| Structure (Denier) | 840*1 | 840*1 |
| Density (Ends/2.5cm) | 28±2 | 28±2 |
| Breaking Tenacity (N/mm) | ≥60 | ≥60 |
| Elongation at break (%) | ≥25 | ≥25 |
| Hot air shrinkage (%) (150℃,3min) | ≤2.5 | ≤2.5 |
| Adhesion (N/cm) | ≥70N/cm |
| Weight (g/m2) | 250±20 |
| Thickness (mm) | 0.48±0.08 |
EPM90
| ITEM | Standard |
| Warp | Weft |
| Material | Nylon6 | Nylon6 |
| Structure (Denier) | 1260*1 | 1260*1 |
| Density (Ends/2.5cm) | 25±2 | 25±2 |
| Breaking Tenacity (N/mm) | ≥90 | ≥90 |
| Elongation at break (%) | ≥25 | ≥25 |
| Hot air shrinkage (%) (150℃,3min) | ≤2.5 | ≤2.5 |
| Adhesion (N/cm) | ≥90N/cm |
| Weight (g/m2) | 325±20 |
| Thickness (mm) | 0.65±0.08 |